Hastelloy（哈氏合金）
|
Alloy |
Ni |
Cu |
Mo |
Cr |
Fe |
W |
Mn |
Si |
C |
other |
|
C-4 |
65 |
0.5* |
16 |
16 |
3* |
- |
1* |
0.08* |
0.01* |
Ti:0.07* |
|
C-22 |
56 |
0.5* |
13 |
22 |
3 |
3 |
0.5* |
0.08* |
0.01* |
V:0.35* |
|
C-276 |
57 |
0.5* |
16 |
16 |
5 |
4 |
1* |
0.08* |
0.01* |
V:0.35* |
|
C-2000 |
59 |
1.6* |
16 |
23 |
3* |
- |
0.5* |
0.08* |
0.01* |
Al: 0.5* |
|
B-3 |
65 |
- |
28.5 |
1.5 |
3 |
3* |
3* |
0.1* |
0.01* |
Al: 0.5* |
|
G-30 |
43 |
2* |
5.5 |
30 |
15 |
2.5 |
1.5* |
1* |
0.03* |
Cb: 1.5* |
|
A-286 |
27 |
|
1.5 |
16 |
Margin |
|
2* |
0.1* |
|
Ti:5* |
|
G-3 |
Margin |
2.5* |
6.8 |
23.5 |
18* |
1.5 |
1* |
1* |
0.015* |
Co:5*
Nb:0.5* |
Note: "*" for the maximum
Reference to the mechanical properties of Hastelloy
|
Grade |
Tensile strength |
Yield strength |
Elongation |
Remarks |
|
бb（Mpa） |
б0.2（Mpa） |
δ5(%) |
|
C-276 |
758 |
363 |
62 |
Annealed state |
|
C-22 |
762 |
390 |
59 |
Annealed state |
|
C-4 |
690 |
310 |
45 |
Annealed state |
|
A-286 |
1080 |
763 |
35 |
Hard state |
☆High temperature corrosion-resistant alloy （Inconel）
The main chemical composition（Wt%）
|
Grade |
Ni |
Cr |
Fe |
Si |
Mn |
Co |
Cu |
Al |
Ti |
Mo |
other |
|
Inconel 600 |
≥72 |
14/17 |
6/10 |
≤0.5 |
≤1.0 |
|
≤0.5 |
|
|
|
C≤0.15 |
|
Inconel 601 |
58/63 |
21/25 |
Margin |
≤0.5 |
≤1.0 |
|
≤1.0 |
1.0-1.7 |
|
|
C≤0.1 |
|
Inconel 625 |
≥58 |
20/23 |
5.0 |
≤0.5 |
≤0.5 |
≤1.0 |
|
≤0.4 |
≤0.4 |
8-10 |
Nb3.15/4.15 |
|
Inconel 686 |
Margin |
19/23 |
1.0 |
≤0.08 |
≤0.75 |
|
|
|
≤0.25 |
15-17 |
W3.0/4.4 |
|
Inconel 690 |
≥58 |
27/31 |
7/11 |
≤0.5 |
≤0.5 |
|
≤0.5 |
|
|
|
|
|
Inconel 718 |
50/55 |
17/21 |
Margin |
≤0.35 |
≤0.35 |
≤1.0 |
≤0.3 |
≤0.9 |
≤1.15 |
2.8/3.3 |
Nb4.75/5.5 |
|
Inconel 751 |
≥70 |
14/17 |
5/9 |
≤0.5 |
≤0.1 |
|
≤0.5 |
≤1.5 |
≤2.6 |
|
Nb1.2 |
|
Inconel 783 |
26/30 |
2.5/3.5 |
24/27 |
≤0.5 |
≤0.5 |
Margin |
|
≤5.6 |
≤0.3 |
|
Nb3.5 |
|
Inconel 800 |
30/35 |
19/23 |
≤39.5 |
≤1.0 |
≤1.5 |
|
≤0.75 |
≤0.6 |
≤0.6 |
|
|
|
Inconel 803 |
32/37 |
25/29 |
Margin |
≤1.0 |
≤1.5 |
|
≤0.75 |
≤0.6 |
≤0.6 |
|
|
|
Inconel 825 |
38/46 |
19.5/23.5 |
≤22 |
≤0.5 |
≤1.0 |
|
≤3.0 |
≤0.2 |
≤1.2 |
≤3.5 |
|
|
Inconel 864 |
30/38 |
20/25 |
Margin |
≤1.0 |
≤1.0 |
|
|
≤1.0 |
≤1.0 |
≤4.8 |
|
|
Inconel 903 |
36/40 |
|
Margin |
|
|
13/17 |
|
≤1.15 |
≤1.85 |
|
Nb≤3.5 |
|
Inconel 908 |
47/51 |
3.75/4.5 |
Margin |
≤0.50 |
≤1.0 |
|
≤0.5 |
≤1.25 |
≤1.80 |
≤0.5 |
Nb≤3.3 |
|
Inconel 909 |
35/40 |
|
|
≤0.50 |
|
12/16 |
|
≤0.15 |
≤1.80 |
|
|
Reference to the mechanical properties of
|
Grade |
Tensile strength |
Yield strength |
Elongation |
Remarks |
|
бb（Mpa） |
б0.2（Mpa） |
δ5(%) |
|
Inconel600 |
655 |
310 |
40 |
Annealed state |
|
Inconel625 |
812 |
345 |
42 |
Annealed state |
|
Inconel718 |
1320 |
1100 |
20 |
statute of limitations |
|
Inconel800 |
552 |
290 |
40 |
Annealed state |
|
Inconel825 |
696 |
286 |
40 |
Annealed state |