☆ The chemical composition of monel:
monel |
Grade |
Ni |
Cr |
Fe |
Si |
Mn |
Co |
Cu |
AL |
Ti |
Mg |
other |
Monel 400 |
≥63 |
|
≤2.5 |
≤0.5 |
≤2.0 |
|
28/34 |
|
|
|
C≤0.3 |
Monel 401 |
40-45 |
|
≤0.75 |
≤0.25 |
≤2.25 |
≤0.25 |
|
|
|
|
C≤0.10 |
Monel 404 |
52-57 |
|
≤0.50 |
≤0.10 |
≤0.10 |
|
|
≤0.05 |
≤0.05 |
|
C≤0.15 |
Monel 405 |
≥63 |
|
≤2.5 |
≤0.50 |
≤2.0 |
|
28/34 |
|
|
|
C≤0.3 |
Monel K500 |
≥63 |
|
≤2.0 |
≤0.50 |
≤1.5 |
|
27/33 |
2.3/3.15 |
≤0.005 |
|
C≤0.25 |
NCu28-2.5-1.5 |
|
|
2.0-3.0 |
≤0.10 |
≤1.8 |
|
27-29 |
|
|
≤0.1 |
C≤0.20 |
NCu40-2-1 |
|
|
≤1.0 |
≤0.15 |
≤2.25 |
|
38-42 |
|
|
|
C≤0.30 |
M-30 |
29-32 |
|
≤1.0 |
≤0.15 |
≤1.2 |
|
|
|
|
|
C≤0.20 |
☆ Monel mechanical properties (room temperature):
Grade |
Tensile strength |
Yield strength |
|
Remarks |
бb(Mpa) |
б0.2(Mpa) |
δ5 (%) |
|
M400 |
550 |
240 |
40 |
Annealed state |
M401 |
441 |
134 |
50 |
Annealed state |
M404 |
440 |
140 |
45 |
Annealed state |
M405 |
550 |
240 |
40 |
Annealed state |
MK500 |
1100 |
790 |
20 |
statute limitations |
NCu28-2.5-1.5 |
538 |
240 |
≥25 |
Annealed state |
NCu40-2-1 |
460 |
160 |
≥30 |
Annealed state |
M-30 |
426 |
140 |
≥38 |
Annealed state | ☆ Corrosion of the monel:
Grade|
Corrosion(mm/y)|Media | |
Hydrofluoric acid 40% 30℃ |
Sulfuric acid
room temperature78% |
NaOH
50% 60℃ |
Monel 400 |
0.1235 |
0.0092 |
0.0005 |
Monel 405 |
0.1109 |
0.0108 |
0.00062 |
Monel k-500 |
0.1236 |
0.0133 |
0.00055 | Can also produce according to the needs of users of the products use different performance
☆ Pure nickel: Pure nickel products, the main component(Wt%)
Grade |
Ni |
Cr |
Fe |
Si |
Mn |
Co |
Cu |
C |
Ti |
Mg |
other |
Nickel 200 |
≥99 |
|
≤0.40 |
≤0.35 |
≤0.35 |
|
≤0.25 |
|
|
|
|
Nickel 201 |
≥99 |
|
≤0.40 |
≤0.35 |
≤0.35 |
|
≤0.25 |
|
|
|
|
Nickel 205 |
≥99 |
|
≤0.20 |
≤0.15 |
≤0.35 |
|
≤0.15 |
|
≤0.05 |
≤0.08 |
|
Nickel 212 |
≥97 |
|
≤0.25 |
≤0.20 |
≤2.5 |
|
≤0.20 |
|
|
≤0.02 |
|
Nickel 270 |
≥99.9 |
|
≤0.05 |
|
≤0.003 |
|
≤0.01 |
|
≤0.005 |
≤0.02 |
|
N4 |
99.9 |
|
|
0.03 |
0.002 |
|
0.015 |
0.01 |
|
0.01 |
|
N6 |
99.5 |
|
|
0.1 |
0.05 |
|
0.06 |
0.1 |
|
0.1 |
|
N8 |
99 |
|
|
0.15 |
0.2 |
|
0.15 |
0.2 |
|
0.1 |
|
Pure nickel reference mechanical properties
grade |
Tensile strength |
Yield strength |
|
Remarks |
бb(Mpa) |
б0.2(Mpa) |
δ5(%) |
Niekel 200 |
462 |
148 |
47 |
Annealed state |
Niekel 201 |
403 |
103 |
50 |
Annealed state |
Niekel 205 |
345 |
90 |
45 |
Annealed state |
Niekel 212 |
423 |
126 |
48 |
Annealed state |
Niekel 270 |
345 |
110 |
50 |
Annealed state |
N4 |
342 |
112 |
50 |
Annealed state |
N6 |
351 |
118 |
50 |
Annealed state |
N8 |
443 |
132 |
48 |
Annealed state |
|
返回 |
|
|
|